FIGURE 4 RIGID WHITE
OVER VIEW
Opaque rigid white production-grade plastic for same-day parts. This biocompatible-capable material provides a smooth surface finish, long-term environmental stability, and long-lasting, clean white color.
Opaque rigid white production-grade plastic for same-day parts. This biocompatible-capable material provides a smooth surface finish, long-term environmental stability, and long-lasting, clean white color.
. Handles and fixtures for medical applications that require biocompatibility
. Electronics enclosures and small components or parts for devices
. Motor housings, covers, guards, snap-fit parts, jigs, fixtures, and other functional prototyping and low volume production parts
.Good long-term environmental stability measured out to 8 years indoor and 2 years outdoor
.Clean, long-lasting, opaque white color
.Fast throughput to finished part; no secondary thermal cure required
.Excellent surface quality, accuracy, and repeatability
. Thermoplastic behavior with necking at break
. 65°C heat deflection temperature
. 20% elongation at break
. Flexural modulus of 2200MPa
. Biocompatible-capable per ISO10993-5 and ISO10993-10
. UL94 HB flammability
. Fast throughput to finished part; no secondary thermal cure required
. Print speeds up to 47 mm/hr at 50-micron layer thickness
The full suite of mechanical properties is given per ASTM and ISO standards where applicable. All parts are conditioned per ASTM recommended standards for a minimum of 40 hours at 23 ¡ÆC, 50% RH. Material properties include physical and mechanical properties, as well as thermal, UL flammability, and electrical (dielectric strength, dielectric constant, dissipation factor, and volume resistivity)
Figure 4 technology prints parts that are isotropic in mechanical properties meaning the parts printed along either the XYZ axis will give similar results. Parts do not need to be oriented to get the highest mechanical properties, improving the degree of freedom for part orientation for mechanical properties.
. Long-term indoor and outdoor environmental (UV and humidity) stability
. Thermoplastic behavior with necking at break
. 65 °C heat deflection temperature
. 20% elongation at break
. Flexural modulus of 2200 MPa
. Isotropic properties
. UL94 HB flammability
. Biocompatible-capable per ISO10993-5 and ISO10993-10
. Print speeds up to 47 mm/hr at 50-micron layer thickness