FIGURE 4 RUBBER-BLK 10
OVER VIEW
High tear strength, malleable material for hard rubber-like parts
High tear strength, malleable material for hard rubber-like parts
. Slow-rebound hard-rubber material allows for multiple touch applications, including grips, handles, bumpers
. Good for strain-relief type applications
. Couplings and over moldings
. Production parts needing long term environmental stability where mechanical properties fit
. Exceptional surface finish
. Very tough material
. Great for soft-touch applications
. Engineered for long term environmental stability
. High tear strength
. Shore hardness of 59D and 97A
. Tough and durable
. Biocompatible capable per ISO10993-5 and ISO10993-10
The full suite of mechanical properties is given per ASTM and ISO standards where applicable. All parts are conditioned per ASTM recommended standards for a minimum of 40 hours at 23 ¡ÆC, 50% RH. Material properties include physical and mechanical properties, as well as thermal, UL flammability, and electrical (dielectric strength, dielectric constant, dissipation factor, and volume resistivity).
Figure 4 technology prints parts that are isotropic in mechanical properties meaning the parts printed along either the XYZ axis will give similar results. Parts do not need to be oriented to get the highest mechanical properties, further improving the degree of freedom for part orientation for mechanical properties.
. Elongation at break: 80%
. Tensile modulus: 540 MPa
. Impact strength (notched Izod): 125 J/m
. Shore hardness: 59D, 97A
. Tear Strength: 76 kN/m
. UL94 HB flammability
. Biocompatible capable per ISO10993-5 and ISO10993-10
. Long-term indoor and outdoor environmental stability